WEPFDV005 Tensile Tests of Large Grain Ingot Niobium at Liquid He Temperature 562
 
  • M. Yamanaka
    KEK, Ibaraki, Japan
  • K. Enami
    Tsukuba University, Ibaraki, Japan
 
  Tensile tests at liquid He temperature were performed using specimen taken from high purity large grain niobium ingot produced by CBMM. The measured RRR is 242. The ingot is 260 mm in diameter and sliced by a multi wire saw to 2.8 thickness. 5 specimens were cut off from one sliced disk. 3 disks were set in same phase to obtain same grain distribution. 3 specimens each of 5 grain patterns 5, 15 in total were used for the tensile test. The tensile test stand using a cryostat and liquid He was manufactured by ourselves. The measured tensile strength varied 379 to 808 MPa. The average value is 611 MPa. The tensile strength at room temperature is 84 MPa. The strength becomes high at low temperature like a fine grain niobium. The specimen includes a grain boundary, and causes the variation of strength. The different result was obtained in same grain patterns. The relationship between crystal orientation and strength is discussed.  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-WEPFDV005  
About • Received ※ 08 June 2021 — Accepted ※ 12 September 2021 — Issue date; ※ 02 May 2022  
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)