THPTEV004 Surface Oxides on Nb and Nb3Sn Surfaces: Toward a Deeper Understanding 836
 
  • Z. Sun, M. Liepe, T.E. Oseroff, R.D. Porter
    Cornell University (CLASSE), Cornell Laboratory for Accelerator-Based Sciences and Education, Ithaca, New York, USA
  • T. Arias, Z. Baraissov, D.A. Muller, N. Sitaraman
    Cornell University, Ithaca, New York, USA
  • C. Dukes
    University of Virginia, Charlottesville, Virginia, USA
  • D. Johnson-McDaniel, M. Salim
    CCMR, Ithaca, New York, USA
 
  Surface oxides on Nb and Nb3Sn SRF cavities, as a thin ’dirty’ layer, could be critical to their performance as suggested by recent theory. Although these oxides have been studied in the past, we intend here to provide a deeper understanding based on a systematic study on coupon samples that have been processed under the different conditions currently used in SRF cavity treatments. Our aim is to obtain a more complete picture of the oxide evolution. This then might help to explain the observed cavity performance variation, and might allow designing a process to achieve a designed, optimized surface with controlled oxides types and thickness. We find that the surface oxides are in amorphous phase that exhibits normal conducting behaviors, while the pentoxide further degrades with time. Also, we observed a thin hydroxide layer on the outermost surface and possibly Nb(OH)x motifs in the bulk. Moreover, distinctive oxide structures were found in Nb3Sn samples from vapor diffusion, electroplating, and sputtering. The semiconducting SnOx appeared through the oxide depth in vapor diffused Nb3Sn, while a ~1 nm SnOx layer merely exists at the outermost surface of electroplated Nb3Sn.  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-THPTEV004  
About • Received ※ 09 July 2021 — Revised ※ 11 August 2021 — Accepted ※ 21 August 2021 — Issue date ※ 04 November 2021
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)