TUPFAV003 Stable Beam Operation at 33 MV/m in STF-2 Cryomodules at KEK 382
 
  • Y. Yamamoto, M. Akemoto, D.A. Arakawa, A. Araki, S. Araki, A. Aryshev, T. Dohmae, M. Egi, M.K. Fukuda, K. Hara, H. Hayano, Y. Honda, T. Honma, H. Ito, E. Kako, H. Katagiri, R. Katayama, M. Kawamura, N. Kimura, Y. Kojima, Y. Kondou, T. Konomi, M. Masuzawa, T. Matsumoto, S. Michizono, Y. Morikawa, H. Nakai, H. Nakajima, K. Nakanishi, M. Omet, T. Oyama, T. Saeki, H. Sakai, H. Shimizu, S.I. Takahara, R. Ueki, K. Umemori, A. Yamamoto
    KEK, Ibaraki, Japan
  • S. Aramoto
    Hiroshima University, Higashi-Hiroshima, Japan
  • M. Kuriki
    Hiroshima University, Graduate School of Science, Higashi-Hiroshima, Japan
  • Z.J. Liptak
    HU/AdSM, Higashi-Hiroshima, Japan
  • K. Sakaue
    The University of Tokyo, The School of Engineering, Tokyo, Japan
  • A. Yamamoto
    CERN, Meyrin, Switzerland
 
  In STF at KEK, as the operational demonstration of the SRF accelerator for ILC, the STF-2 cryomodules (CM1+CM2a: one and half size CM with 12 cavities) have achieved 33 MV/m as average accelerating gradient with 7 cavities in Mar/2019. After that, one cavity with the lowest performance installed in CM2a was replaced with one N-infused cavity developed for High-Q/High-G R&D between Japan and US. From this April, the beam operation started again and those CMs achieved 33 MV/m as average accelerating gradient with 9 cavities including one N-infused cavity again. This is the very important milestone for ILC. In this report, the detailed results will be presented.  
poster icon Poster TUPFAV003 [3.015 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-TUPFAV003  
About • Received ※ 21 June 2021 — Revised ※ 11 July 2021 — Accepted ※ 21 August 2021 — Issue date ※ 01 November 2021
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
MOPCAV004 Mechanical Properties of Directly Sliced Medium Grain Niobium for 1.3 GHz SRF Cavity 259
 
  • A. Kumar, K. Abe, T. Dohmae, S. Michizono, T. Saeki, Y. Watanabe, A. Yamamoto, M. Yamanaka
    KEK, Ibaraki, Japan
  • A. Fajardo, N. Lannoy
    ATI, Albany, Oregon, USA
  • G.R. Myneni
    JLab, Newport News, Virginia, USA
  • G.R. Myneni
    BSCE, Yorktown, Virginia, USA
 
  At KEK, research is being conducted to manufacture cost-effective 1.3 GHz superconducting radio frequency cavities based on the fine grain (FG) and large grain (LG) Niobium (Nb) materials. Medium grain (MG) Nb has been proposed and developed as an alternative to the FG and LG Nb, being expected to have better mechanical stability with a cost-effective and clean manufacturing approach. MG Nb has an average grain size of 200 - 300 µm, which is approximately 100 times smaller than the LG Nb, however, there are occasional grains as large as 1-2 mm. As such, it is expected to have isotropic properties rather than the anisotropic properties of LG Nb. In this paper, we will outline the mechanical properties of the directly sliced high RRR MG Nb material (manufactured by ATI), and a comparative study will be presented with respect to FG and LG Nb. Moreover, the viability of MG Nb for the global high-pressure regulation for 1.3 GHz SRF cavity will be presented.  
poster icon Poster MOPCAV004 [1.791 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-MOPCAV004  
About • Received ※ 21 June 2021 — Revised ※ 11 July 2021 — Accepted ※ 21 August 2021 — Issue date ※ 25 March 2022
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
MOPCAV012 Fabrication of 1.3 GHz SRF Cavities Using Medium Grain Niobium Discs Directly Sliced from Forged Ingot 287
 
  • T. Dohmae, K. Abe, H. Inoue, A. Kumar, S. Michizono, T. Saeki, K. Umemori, Y. Watanabe, A. Yamamoto, M. Yamanaka, K. Yoshida
    KEK, Ibaraki, Japan
  • A. Fajardo, N. Lannoy
    ATI, Albany, Oregon, USA
  • G.R. Myneni
    JLab, Newport News, USA
 
  Medium grain (MG) niobium disc which is directly sliced from forged ingot is newly investigated for the cavity material. An effective cost reduction can be achieved using MG niobium since rolling process which is necessary for typical niobium sheet can be skipped during MG niobium production. Grain size of MD niobium is 200-300 um which is much smaller than large grain (LG) niobium directly sliced from melted niobium ingot. Hence, the formability of MG niobium is expected to be much better than LG niobium. KEK has started fabrication of cavity using MG niobium. In this talk, characteristic of MG niobium during fabrication will be reported.  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-MOPCAV012  
About • Received ※ 20 June 2021 — Revised ※ 12 July 2021 — Accepted ※ 21 August 2021 — Issue date ※ 17 September 2021
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)