MOPCAV002 Shape Evolution of C75 Large-Grain Niobium Half-Cells During Cavity Fabrication cavity, laser, software, cryomodule 255
 
  • G. Ciovati
    JLab, Newport News, Virginia, USA
 
  Funding: U.S. Department of Energy, Office of Science, Office of Nuclear Physics under contract DE-AC05-06OR23177.
The largely anisotropic deformation of large-grain Nb discs during deep drawing into half-cells poses a challenge for achieving a desired shape accuracy. Two 5-cell cavities for the C75 CEBAF cryomodule rework program have been fabricated at Jefferson Lab from large-grain Nb discs directly sliced from an ingot. The shape of the inner surface of eight half-cells has been inspected using a FARO Edge laser scanner during the fabrication process and compared to the reference shape. On average, approximately 63% of the half-cell inner surface was found to be within 0.1 mm of the reference shape and ~90% to be within 0.2 mm, after the final equator machining. Several 5-cell C75 cavities have also been fabricated at Research Instruments, Germany, and measurements of the shape accuracy using a Zeiss 3D coordinate measuring machine gave similar results. One half-cell was measured both at Research Instruments and Jefferson Lab for comparison.
 
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-MOPCAV002  
About • Received ※ 21 June 2021 — Accepted ※ 21 August 2021 — Issue date; ※ 11 February 2022  
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
THPCAV001 Modal Analysis and Vibration Test of Single Spoke Resonator Type-1 (SSR1) for RISP cavity, SRF, simulation, superconductivity 776
 
  • M.O. Hyun, Y.W. Jo, H.C. Jung, Y. Kim, M. Lee
    IBS, Daejeon, Republic of Korea
 
  Funding: This paper was supported by the Rare Isotope Science Project (RISP), which is funded by the Ministry of Science and ICT (MSIT) and National Research Foundation (NRF) of the Republic of Korea.
Rare Isotope Science Project (RISP) is developing the single spoke resonator type-1 (SSR1) and type-2 (SSR2) for making superconducting linear accelerator 2 (SCL2). For optimizing of SSR1 and SSR2, we should research every aspects of superconducting cavity including RF performances and mechanical properties. This paper explains about modal analysis of SSR1 using FEM (finite element method) applying material properties of RRR300 niobium for bare cavity and STS316L for liquid helium jacket. Also, this paper shows the vibration test results with modal analysis.
 
poster icon Poster THPCAV001 [1.636 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-THPCAV001  
About • Received ※ 22 June 2021 — Accepted ※ 06 September 2021 — Issue date; ※ 15 May 2022  
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)