Paper Title Other Keywords Page
SUPCAV009 First Nb3Sn Coating and Cavity Performance Result at KEK cavity, SRF, radio-frequency, experiment 27
 
  • K. Takahashi, T. Okada
    Sokendai, Ibaraki, Japan
  • H. Ito, E. Kako, T. Konomi, H. Sakai, K. Umemori
    KEK, Ibaraki, Japan
 
  At KEK, Nb3Sn vapor diffusion R&D for High-Q has just started. We have performed Nb3Sn coating on niobium samples and characterized these samples. We optimized the cavity coating parameter from the result of characterized samples. After optimizing the parameter, we have performed Nb3Sn coating on a TESLA-like single-cell Nb cavity and measured cavity performance in vertical tests. This presentation presents the result of the cavity coating and performance results.  
poster icon Poster SUPCAV009 [1.477 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-SUPCAV009  
About • Received ※ 21 June 2021 — Accepted ※ 18 March 2022 — Issue date; ※ 16 May 2022  
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
TUPCAV004 Deflecting Cavities for Proton Beam Spreader in CiADS Project cavity, proton, dipole, linac 445
 
  • Y.L. Huang, Y. He, H. Jia, Y.S. Qin, Z.J. Wang, Z.L. Zhang
    IMP/CAS, Lanzhou, People’s Republic of China
 
  Funding: Large Research Infrastructures "China initiative Accelerator Driven System’(Grant No.2017-000052-75-01-000590 ) and National Natural Science Foundation of China (Grant NO. 11805249)
Chinese initiative Accelerator Driven Subcritical System (CiADS) is supposed to accelerate continuous 162.5 MHz, 10 mA (or higher) proton beam to 500 MeV (or higher energy) with a superconducting driver linac. More application scenarios based on this high power intensity proton linac are now under considerations. Beam spreader system based on deflecting cavities for multiple users simultaneous operation are discussed in this paper, as well as the RF structure options for the equal eight- and nigh- beam-line split schemes.
#huangyulu@impcas.ac.cn
 
poster icon Poster TUPCAV004 [1.074 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-TUPCAV004  
About • Received ※ 21 June 2021 — Revised ※ 16 August 2021 — Accepted ※ 23 August 2021 — Issue date ※ 13 May 2022
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
TUPTEV009 Seamless 1.3 GHz Copper Cavities for Nb Coatings: Cold Test Results of Two Different Approaches cavity, SRF, niobium, ISOL 498
 
  • L. Vega Cid, S. Atieh, L.M.A. Ferreira, L. Laín-Amador, C. Pereira Carlos, G.J. Rosaz, K. Scibor, W. Venturini Delsolaro, P. Vidal Garcia
    CERN, Meyrin, Switzerland
  • S.B. Leith
    University Siegen, Siegen, Germany
 
  A necessary condition for high SRF performances in thin film coated cavities is the absence of substrate defects. For instance, in the past, defects originated around electron beam welds in high magnetic field areas have been shown to be the cause of performance limitations in Nb/Cu cavities. Seamless cavities are therefore good candidates to allow an optimization of the coating parameters without the pitfalls of a changing substrate. In this work, we present the first results of two different methods to produce seamless cavities applied to 1.3 GHz copper single cells coated with thin Nb films by means of HIPIMS. A first method consists in electroplating the copper resonator on precisely machined aluminum mandrels, which are then dissolved chemically. As an alternative and a cross check, one cavity was machined directly from the bulk. Both cavities were coated with HIPIMS Nb films using the same coating parameters and the SRF performance was measured down to 1.8 K with a variable coupler to minimize the measurement uncertainty.  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-TUPTEV009  
About • Received ※ 21 June 2021 — Revised ※ 28 October 2021 — Accepted ※ 18 November 2021 — Issue date ※ 10 February 2022
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
WEPFDV010 Structural Investigation of Nitrogen-Doped Niobium for SRF Cavities cavity, niobium, SRF, operation 581
 
  • M. Major, L. Alff, M. Arnold, J. Conrad, S. Flege, R. Grewe, N. Pietralla
    TU Darmstadt, Darmstadt, Germany
 
  Funding: Work supported by the German Federal Ministry for Education and Research (BMBF) through grant 05H18RDRB2 and the German Research Foundation (DFG) via the AccelencE Research Training Group (GRK 2128).
Niobium is the standard material for superconducting RF (SRF) cavities for particle acceleration. Superconducting materials with higher critical temperature or higher critical magnetic field allow cavities to work at higher operating temperatures or higher accelerating fields, respectively. One direction of search for new materials with better properties is the modification of bulk niobium by nitrogen doping. In the Nb-N phase diagram, the cubic delta-phase of NbN has the highest critical temperature. Niobium samples were annealed and doped with nitrogen in the high-temperature furnace at TU Darmstadt and investigated at its Materials Research Department with respect to structural modifications. X-ray diffraction (XRD) confirmed the appearance of Nb4N3 and Nb2N phases on the surface of the samples. A single cell cavity was annealed under optimized doping conditions. The test samples treated together with the cavity showed almost single Nb4N3 phase. XRD pole figures also showed grain growth during sample annealing.
 
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-WEPFDV010  
About • Received ※ 22 June 2021 — Revised ※ 18 August 2021 — Accepted ※ 17 November 2021 — Issue date ※ 19 November 2021
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
THPCAV006 Recent Activities Regarding 9-Cell TESLA-Type Cavities at KEK cavity, EPICS, controls, niobium 792
 
  • M. Omet, R. Katayama, K. Umemori
    KEK, Ibaraki, Japan
 
  In this contribution we report on two topics regarding recent activities on 9-cell TESLA-type cavities at the High Energy Accelerator Research Organization (KEK). First, we give an overview of the inner surface treatments and vertical test (VT) results of four fine grain 9-cell TESLA-type cavities over the last one and a half years. Secondly, we report on the upgrade of the VT DAQ system at the Superconducting RF Test Facility (STF) at KEK. In this upgrade, most components of the VT system were integrated in an EPICS control system. Based on Control System Studio (CSS) and Python a new user interface was created, improving the workflow during and after VTs at STF.  
poster icon Poster THPCAV006 [1.748 MB]  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-THPCAV006  
About • Received ※ 18 June 2021 — Revised ※ 26 August 2021 — Accepted ※ 23 November 2021 — Issue date ※ 04 March 2022
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)  
 
FROFDV01 Systematic Investigation of Mid-T Furnace Baking for High-Q Performance cavity, niobium, vacuum, SRF 881
 
  • H. Ito, A. Araki, K. Umemori
    KEK, Ibaraki, Japan
  • K. Takahashi
    Sokendai, Ibaraki, Japan
 
  We report on an investigation of the effect of a new baking process called "furnace baking" on the quality factor. Furnace baking is performed as the final step of the cavity surface treatment; the cavities are heated in a vacuum furnace in a temperature range of 200-800C for 3 h, followed by high-pressure rinsing and radio-frequency measurement. We find the anti-Q-slope for cavities furnace-baked at a temperature range of 250 to 400C and a reduction in the residual resistance for all cavities. In particular, an extremely high Q value of 5·1010 at 16 MV/m and 2.0 K is obtained for cavities furnace-baked at 300C.  
DOI • reference for this paper ※ https://doi.org/10.18429/JACoW-SRF2021-FROFDV01  
About • Received ※ 21 June 2021 — Accepted ※ 24 February 2022 — Issue date; ※ 30 April 2022  
Cite • reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml)